Alloidhean nicil TIG ERNiCr-3 Uidheam stuthan soldering
COMPONET CEIMICEAL:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+ta | P | S |
RIAGHAILTEAN GB/T | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | - | - |
RIAGHAILTEAN AWS | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | 0.03 | 0.015 |
LUACH EISIMPLEIR | 0.024 | 2.78 | 0.05 | 20.69 | 72.85 | 0.15 | 0.67 | 2.44 | 0.001 | 0.001 |
Seilbh Meicnigeach:
LAOIDHEAN | neart toraidh (MPa) | Neart leudachaidh (MPa) | LUACH IMAPACT J/ ℃ | ELONGATION(%) | ||||
RIAGHAILTEAN GB/T | - | - | - | - | ||||
RIAGHAILTEAN AWS | - | - | - | - | ||||
LUACH EISIMPLEIR | - | 710 | 170-196 | 39 |
Uèir tàthaidh gas alloy Nickel-chromium-iarann nickel-base, is e co-dhèanamh ainmichte 72% Ni-20% Cr-3% Mn-2.5% Nb + Ta.
Tha deagh fheartan meacanaigeach aig a’ mheatailt leaghte, deagh sheasamh an aghaidh creimeadh, neart oxidation àrd agus neart èaladh.
Arc seasmhach, cumadh breagha, sruthadh math de iarann leaghte, le coileanadh pròiseas tàthaidh sàr-mhath.
-
Qinghai Youjian Wunan Oilfield
-
Stuthan tàthaidh airson botail carbaid LNG
-
Teasadair cuideam àrd de Hangzhou Boiler Group Co. LTD
COMPONET CEIMICEAL:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+ta | P | S |
RIAGHAILTEAN GB/T | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | - | - |
RIAGHAILTEAN AWS | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | 0.03 | 0.015 |
LUACH EISIMPLEIR | 0.024 | 2.78 | 0.05 | 20.69 | 72.85 | 0.15 | 0.67 | 2.44 | 0.001 | 0.001 |
Seilbh Meicnigeach:
LAOIDHEAN | neart toraidh (MPa) | Neart leudachaidh (MPa) | LUACH IMAPACT J/ ℃ | ELONGATION(%) | ||||
RIAGHAILTEAN GB/T | - | - | - | - | ||||
RIAGHAILTEAN AWS | - | - | - | - | ||||
LUACH EISIMPLEIR | - | 710 | 170-196 | 39 |